12Cr1MoV鋼在堿金屬硫氯鹽中的腐蝕行為
          
Corrosion Behavior of 12Cr1MoV Steel in Alkali Metal Sulfur-chloride Salt

摘    要
將12Cr1MoV鋼在不同溫度(500,550,600℃)、不同組成的KCl-K2SO4熔鹽中進行腐蝕試驗,研究了溫度和熔鹽組成對試驗鋼腐蝕動力學、腐蝕形貌和腐蝕產物的影響。結果表明:隨溫度的升高或熔鹽中K2SO4含量的增加,試驗鋼的腐蝕加??;在600℃ KCl-25% K2SO4(質量分數,下同)熔鹽中腐蝕后,試驗鋼表面存在大量的孔洞,腐蝕產物呈顆粒狀,而在600℃ KCl-75% K2SO4熔鹽中腐蝕后,表面孔洞較少,腐蝕產物呈片狀;在600℃ KCl-25% K2SO4熔鹽中腐蝕后,試驗鋼呈現非均勻腐蝕形貌,在550℃和500℃下呈現均勻腐蝕形貌,腐蝕內層主要由鐵、鉻氧化物組成,鉻元素含量隨溫度升高而減少;在550℃ KCl-75% K2SO4熔鹽中腐蝕形成的腐蝕內層厚度為83.8 μm,比在550℃ KCl-25% K2SO4熔鹽中形成的厚了近1倍,且腐蝕內層更致密、孔洞更小。
標    簽 生物質   鍋爐   12Cr1MoV鋼   堿金屬熔鹽   腐蝕   biomass   boiler   12Cr1MoV steel   alkali metal molten salt   corrosion  
 
Abstract
Corrosion tests in KCl-K2SO4 molten salts with different composition at different temperatures (500, 550, 600℃) were conducted on 12Cr1MoV steel. The effects of temperature and molten salt composition on corrosion kinetics, corrosion morphology and corrosion products of the tested steel were studied. The results show that with the rise of temperature or with the increase of K2SO4 content in molten salts, the corrosion of the tested steel increased. After corrosion in KCl-25wt%K2SO4 molten salt at 600℃, a large number of holes existed on surface of the tested steel and the corrosion products were granular; after corrosion in KCl-75wt%K2SO4 molten salt at 600℃, few holes existed on surface of the tested steel and the corrosion products were flake. The tested steel presented uneven corrosion morphology after corrosion in KCl-25wt%K2SO4 molten salt at 600℃ while showed uniform corrosion morphology at 550℃ and 500℃. The inner corrosion layer was composed of oxides of Fe and Cr, and the Cr content decreased with the temperature rising. The thickness of inner corrosion layer formed during corrosion in KCl-75wt%K2SO4 molten salt at 550℃ was 83.8 μm, nearly twice that formed in KCl-25wt%K2SO4 molten salt at 550℃, and the inner corrosion layer was relatively dense and the holes were relatively small.

中圖分類號 TG178   DOI 10.11973/jxgccl201811001

 
  中國光學期刊網論文下載說明


所屬欄目 試驗研究

基金項目 國家自然科學基金資助項目(51275058)

收稿日期 2017/8/3

修改稿日期 2018/7/13

網絡出版日期

作者單位點擊查看

備注王剛(1992-),男,江蘇連云港人,碩士研究生

引用該論文: WANG Gang,HE Jianjun,LI Wei,LIU Chen,LIU Zhenyao. Corrosion Behavior of 12Cr1MoV Steel in Alkali Metal Sulfur-chloride Salt[J]. Materials for mechancial engineering, 2018, 42(11): 1~5
王剛,何建軍,李微,劉晨,劉震瑤. 12Cr1MoV鋼在堿金屬硫氯鹽中的腐蝕行為[J]. 機械工程材料, 2018, 42(11): 1~5


論文評價
共有人對該論文發表了看法,其中:
人認為該論文很差
人認為該論文較差
人認為該論文一般
人認為該論文較好
人認為該論文很好
分享論文
分享到新浪微博 分享到騰訊微博 分享到人人網 分享到 Google Reader 分享到百度搜藏分享到Twitter

參考文獻
【1】武岳, 王永征, 栗秀娟, 等. 生物質混煤燃燒鍋爐過熱器受熱面金屬氯腐蝕特性[J]. 動力工程學報, 2014, 34(9):690-695.
 
【2】AHO M, PAAKKINEN K, TAIPALE R. Quality of deposits during grate combustion of corn stover and wood chip blends[J]. Fuel, 2013, 104:476-487.
 
【3】MONTGOMERY M,LARSEN O H. Field test corrosion experiments in Denmark with biomass fuels(Ⅱ):Co-firing of straw and coal[J]. Materials and Corrosion, 2002, 53(3):185-194.
 
【4】HANSEN P F B,ANDERSEN K H,WIECK-HANSEN K,et al. Co-firing straw and coal in a 150 MW utility boiler:In situ measurements[J]. Fuel Processing Technology,1998,54(1):207-225.
 
【5】李琰, 魯金濤, 楊珍, 等. 鍋爐奧氏體不銹鋼在模擬煤灰和高硫煙氣環境中腐蝕行為的研究[J]. 動力工程學報, 2017, 37(2):156-162.
 
【6】NIELSEN H P, BAXTER L L, SCLIPPAB G, et al. Deposition of potassium salts on heat transfer surfaces in straw-fired boilers:A pilot-scale study[J]. Fuel, 2000, 79(2):131-139.
 
【7】METSÄJOKI J, HUTTUNEN-SAARIVIRTA E, LEPISTÖ T. Elevated-temperature corrosion of uncoated and aluminized 9%-12% Cr boiler steels beneath KCl deposit[J]. Fuel, 2014, 133:173-181.
 
【8】ANTUNES R A, DE OLIVEIRA M C L. Corrosion in biomass combustion:A materials selection analysis and its interaction with corrosion mechanisms and mitigation strategies[J]. Corrosion Science, 2013, 76:6-26.
 
【9】NIELSEN H P, FRANDSEN F J, DAM-JOHANSEN K. Lab-scale investigations of high-temperature corrosion phenomena in straw-fired boilers[J]. Energy & Fuels, 1999, 13(6):1114-1121.
 
【10】FANG W C, RAPP R A. Electrochemical reactions in a pure Na2SO4 melt[J]. Journal of the Electrochemical Society, 1983, 130(12):2335-2341.
 
【11】李萍, 李安娜, 龐勝嬌, 等. Super304H抗堿金屬硫酸鹽的腐蝕行為[J]. 材料工程, 2015, 43(1):54-58.
 
【12】盧旭東, 田素貴, 陳濤, 等. 高鉻鎳基合金熔融硫酸鹽熱腐蝕過程中內氧化和內硫化行為的研究[J]. 稀有金屬材料與工程, 2014, 43(1):79-84.
 
【13】李灼賢, 王準, 余春江. 生物質鍋爐典型過熱器金屬材料表面鈍化膜腐蝕特性研究[J]. 能源工程, 2015(3):34-37.
 
相關信息
   標題 相關頻次
 漢代銅鏡的耐蝕性分析
 4
 12Cr1MoV鋼在高溫混合堿金屬氯鹽中的熱腐蝕行為
 3
 高壓汽包爐水冷壁爆管原因分析
 3
 顆粒粒徑對噴射沉積制備SiC顆粒增強鋁硅合金復合材料顯微組織及拉伸性能的影響
 3
 Φ219mm×10.5mm彎管環焊縫穿孔失效分析
 2
 1 000 MPa級超高強度熱鍍鋅鋼板耐腐蝕性能
 2
 1050A鋁合金模擬海洋大氣環境腐蝕行為的中性鹽霧試驗
 2
 1050A鋁合金在模擬海洋大氣環境中周浸腐蝕行為
 2
 10號碳鋼在NaOH溶液中的腐蝕電化學行為
 2
 12Cr1MoV鋼高溫過熱器管爆裂分析
 2
 12Cr1MoV鋼過熱器爆管的顯微組織和力學性能
 2
 12Cr1MoV珠光體耐熱鋼長期服役中碳化物的變化及對性能的影響
 2
 12Cr-F/M鋼在超臨界水中的腐蝕行為
 2
 13Cr不銹鋼與Ni基合金油管表面擦劃傷的腐蝕行為
 2
 14Cr1MoR鋼在高溫硫環境中的失效行為
 2
 15CrMo鋼和12Cr1MoV鋼的快速金相制樣方法
 2
 16MnR鋼在多種回填材料中的腐蝕行為
 2
 16Mn鋼在管輸俄羅斯原油析出水中的腐蝕行為
 2
 201型不銹鋼在酸性食物模擬環境中的腐蝕行為
 2
 20G/316L雙金屬復合管失效的原因
 2
 20號鋼在HCl-H2S-H2O溶液中的腐蝕行為
 2
 20號鋼在氣田站場分離器積液中的腐蝕行為
 2
 220kV鋼芯鋁絞線斷股事故化學分析
 2
 2507雙相不銹鋼鉀鹽蒸發罐腐蝕的原因分析
 2
 2A12鋁合金當量加速腐蝕試驗
 2
 2-甲基咪唑啉及其復配緩蝕劑在高硬度電解質水溶液中的緩蝕性能
 2
 304H彈簧鋼絲及彈簧表面腐蝕的原因
 2
 304L不銹鋼焊接接頭表面狀態對其在硼酸溶液中腐蝕行為的影響
 2
 304奧氏體不銹鋼高溫拉伸變形時的鋸齒流變行為
 2
 304不銹鋼在高溫環烷酸介質中的腐蝕行為
 2
白小姐六肖中特免费公开资料 广东快乐十分历史开奖结果 浙江十一选五 大数据龙头股票有哪 河内5分彩243553公平 浙江体彩玩法介绍大全 广东南粤好彩1开奖结果 体彩论坛 炒股入门与技巧 广西十一选五 时时彩软件杀百十位