X70管線鋼在近中性及高pH值溶液中的電化學行為和SCC敏感性
          
ELECTROCHEMICAL BEHAVIOUR AND SCC SUSCEPTIBILITY OF PIPELINE STEEL X70 IN NEAR-NEUTRAL AND HIGH pH SOLUTIONS

摘    要
采用動電位極化曲線測試法研究了溫度、通氣條件和pH值對X70管線鋼在NS4溶液和0.5 mol/L Na2CO3+1 mol/L NaHCO3溶液中的電化學極化行為的影響,并用慢應變速率試驗(SSRT)研究了X70管線鋼在這些溶液中的應力腐蝕破裂(SCC)敏感性.結果表明,X70管線鋼在NS4溶液中不出現活化—鈍化轉變區,隨外加電位負移, SCC敏感性增加,表現出氫致破裂(HIC)的特征;在0.5 mol/L Na2CO3+1 mol/L NaHCO3高pH值溶液中出現活化—鈍化轉變區,在陰極極化區,也表現出氫致破裂(HIC)的特征,但在陽極極化區,發生的是陽極溶解型應力腐蝕破裂(ADSCC).
標    簽 管線鋼   近中性溶液   高pH值溶液   電化學行為   SCC敏感性   Pipeline steel   High-pH solution   NS4 solution   Electrochemical behavior   SCC susceptibility  
 
Abstract
The influence of temperature,aerated condition and pH value on the electrochemical behavior and stress corrosion cracking(SCC) susceptibility of X70 pipeline steel in NS4 solution and 0.5 mol/L Na2CO3+1 mol/L NaHCO3 solution was investigated using potentiodynamic polarization measurements and slow strain rate tests(SSRT).In NS4 solution,active-passive transition behavior did not appear and SCC susceptibility increased with the negative movement of applied potential,indicating character of hydrogen induced cracking(HIC).In 0.5 mol/L Na2CO3+1 mol/L NaHCO3 solution,active-passive transition behavior was found in the potentiodynamic polarization curves,character of hydrogen induced cracking(HIC) was shown in cathodic polarization region and anodic dissolution SCC(ADSCC) occurred in anodic polarization region.

中圖分類號 TG172.6

 
  中國光學期刊網論文下載說明


所屬欄目 試驗研究

基金項目 國家重點基礎研究專項經費(G19990650)、上海市科技發展基金項目(025258036)、上海市自然科學基金(02ZE14031)資助

收稿日期 2006/7/4

修改稿日期

網絡出版日期

作者單位點擊查看

引用該論文: ZHOU Jian-jiang,LIU Xing,LI Guang-fu,GUO Hao,YANG Wu. ELECTROCHEMICAL BEHAVIOUR AND SCC SUSCEPTIBILITY OF PIPELINE STEEL X70 IN NEAR-NEUTRAL AND HIGH pH SOLUTIONS[J]. Corrosion & Protection, 2007, 28(1): 1~5


論文評價
共有人對該論文發表了看法,其中:
人認為該論文很差
人認為該論文較差
人認為該論文一般
人認為該論文較好
人認為該論文很好
分享論文
分享到新浪微博 分享到騰訊微博 分享到人人網 分享到 Google Reader 分享到百度搜藏分享到Twitter

參考文獻
【1】Kentish P J.Gas pipeline failures:Australian experience[J].Br Corros J,1985,20(3):139-146.
 
【2】National Energy Board (NEB),Public inquiry concerning stress corrosion cracking on canadian oil and gas pipelines[G]//NEB Report Mh-2-95,Calgary,AB,Canada:1996.
 
【3】King F,Boven G V,Jack T,et al.Predicting the growth of low-and high pH SCC on gas transmission pipelines based on operating conditions[G]// Proceeding of the CORROSION/2003 Research Topical Symposium:Modeling and Prediction of Lifetimes for Corrodible Structure.Houston:NACE international,2003:127-155.
 
【4】J A Beavers,Carolyn L Durr,Burke S Delanty.High-pH SCC:temperature and potential dependence for cracking in field environments[G]// ASME International Pipeline Conference-Volume 1,1998.
 
【5】Charles E A,Parkins R N.Generation of stress corrosion cracking environments at pipeline surface[J].Corrosion,1995,51(7):518-527.
 
【6】Parkins R N.Predictive approaches to stress corrosion cracking failure[J].Corrosion Science,1980,20(5):151-157.
 
【7】Sutcliffe J M,Fessler R R,Boyd W K,et al.Stress corrosion cracking of carbon steel in carbonate solutions[J].Corrosion,1972,28(8):313-320.
 
相關信息
   標題 相關頻次
 溶解氧對X70管線鋼在高pH值溶液中的電化學行為和SCC敏感性的影響
 16
 電極電位和溫度對X70鋼在高pH值模擬土壤環境中應力腐蝕破裂的影響
 8
 循環載荷作用下X70管線鋼在近中性溶液中應力腐蝕裂紋的擴展行為
 6
 異材焊接件A508III-52M-316L基本材料在高溫水環境中的電化學特性
 5
 奧氏體不銹鋼里氏硬度、維氏硬度及強度之間的換算關系
 4
 國產SA-508Ⅲ低合金鋼在模擬核電高溫水服役環境中的應力腐蝕破裂及力學行為
 4
 硫酸根離子和電極電位對異材焊接件A508/52M在高溫水中應力腐蝕破裂的影響
 4
 埋地重要管線的腐蝕與防護
 4
 水中雜質和電極電位對國產SA-508Ⅲ 低合金鋼在模擬一回路高溫水環境中應力腐蝕破裂的影響
 4
 銅表面超疏水和超親油銀膜的制備和性能
 3
 16MND5/309L/308L/Z2CND18-12N異種金屬焊接件的組織和性能
 2
 200 ℃回火對X80管線鋼在NaHCO3溶液中電化學腐蝕的影響
 2
 2-吡啶甲酸在玻碳電極表面的電化學行為
 2
 7020鋁合金應力腐蝕開裂特征
 2
 AZ31和AZ61鎂合金在MgSO4溶液中的電化學行為對比
 2
 AZ31鎂合金在Al(NO3)3溶液中的電化學行為和放電性能
 2
 AZ91D鎂合金在SO2薄液膜下的電化學腐蝕行為
 2
 GCr15鋼磨削開裂的特征及影響因素
 2
 K60、X80管線鋼連鑄坯的高溫塑性
 2
 L360MCS鋼在普光氣田凝析水中的腐蝕行為
 2
 L360管線鋼在普光氣田集輸系統的腐蝕
 2
 X52管線鋼抗氫致開裂試驗裂紋成因分析
 2
 X52管線鋼熱軋板卷表面裂紋成因分析
 2
 X70管線鋼管件制造熱過程中的形變規律
 2
 X80鋼及其焊縫組織在酸性土壤中的電化學行為
 2
 X80鋼在大港鹽堿土模擬溶液中的腐蝕電化學行為
 2
 表面處理對40Cr鋼腐蝕疲勞壽命的影響
 2
 丙炔醇對AZ31鎂合金陽極電化學行為的影響
 2
 不同電阻率土壤中管線鋼的自腐蝕速率分布
 2
 不同鋼種真實應力屈強比與工程應力屈強比的測試與對比
 2
白小姐六肖中特免费公开资料